毕节耐火漂珠 高温铸造发热冒口漂珠厂家报价 40-100目细漂珠的主要用途 滑，热导率小，耐火度高、保温绝缘、应力应变均匀等多种功能，广泛用于耐火、保温材料的生产和在塑料、涂料、油漆油墨、陶瓷、封装材料、地板胶、石油钻探等领域作增强性填充料。能既有效地改善产品性能或施工效果，又明显地降低生产成本，现已广泛应用于耐火材料的原料之中。

【漂珠特性】

1、高耐火度：漂珠的主要化学成分为硅、铝的氧化物，其中二氧化硅（SiO2)约为50-65%，三氧化s, plastic activation fillers, insulation of high temperature and high pressure, etc.
5, coating industry, paint, printing ink, adhesives, stealth coatings, insulating paint, anti-corrosion paint, floor paint, high temperature resistant fire retardant paint, exterior paint, insulation paint, floor paint, auto putty, putty, etc.
Development: 6, space and space satellite, rocket, the spacecraft surface composites, satellite fire protection layer, Marine equipment, vessels, deep-sea submarines.
7, the plastics industry, such as automotive trim, instrument panel, home appliance shell, fan, speakers, lamps and lanterns is always bearing, casting, gear, structure, zippers, pipes, plates, etc.
8, glass fiber reinforced plastic products: all kinds of glass fiber reinforced plastic products, artificial marble, glass fiber reinforced plastic ship, arts and crafts, etc.CO2等)，热传导极慢极微。所以漂珠不但质轻(容重250-450kg/m3)，而且保温隔热(导热系数常温0.08-0.1)，这为其在轻质保温隔热材料领域大显身手奠定了基础。

3、硬度大、强度高：由于漂珠是以硅铝氧化物矿物相(石英和莫来石)形成的坚硬玻璃体，硬度可达莫氏6-7级，静压强度高达70-140MPa，真密度2.10-2.20g/cm3，因此，漂珠具有很高的强度。一般轻质多孔或中空材料如珍珠岩、沸岩、硅藻土、海浮石、膨胀蛭石等均是硬度的开发和应用，其市场前景非常广阔。 溶解非离子聚丙烯酰胺粉末注意要点: 1、先用常温的自来水将聚丙烯酰胺溶解,非离子型聚丙烯酰胺通常溶解浓度为0.1%,阳离子絮凝剂为0.2%;提高温度可稍微促进溶解,但水温不宜超过50度,水温过高会使PAM产生热降解,从而影响使用效果。 2、加水至溶解槽容积的一半,开启搅拌器进行搅拌。将准确称重的絮凝剂沿搅拌产生的漩涡边缘平静且迅速地倒入。加水到位置,调整到特定浓度。继续搅拌到聚丙烯酰胺絮凝剂完全溶解。 3、搅拌速度:理想的搅拌转速为每分钟200至400转。如转速太快可能会破坏PAM分子。 4、聚丙烯酰胺通常需要约1-2小时的搅拌时间才能使粉末充分溶解。PAM混合不充分或者结团可能影响其它的使用性能,甚至可能产生沉积、阻塞管道和加药泵。 5、在输送水溶液时应避免使用离心泵,禁止使用齿轮泵,否则,溶液在输送时会降低分子量。配成溶解后应在48小时内用完。 聚丙烯酰胺的原理和使用 、絮凝剂、阳离子聚丙烯酰胺等是我差、强度差，用其制的保温隔热制品或轻质耐火制品，都有强度差的缺点。他们的短处恰恰是漂珠的长处，所以漂珠就更有竞争优势，用途更广。

4、电绝缘性，不导电：选去磁珠后的漂珠，是性能的绝缘材料，不导电。一般绝78